1100C CALCIUM SILICATE INSULATION BOARD
![](images/UpFile/2016-3/20163221018140.jpg)
1100C CALCIUM SILICATE INSULATION BOARD
Using silica fume(microsilica) ,quartz and lime as raw material, synthesized through dynamic hydrothermal process, reinforced with glass fibre and paper fibre , ca-si-board is formed by press.Amorphous silica fill up interspace between Xonotlite crystal ,it heighten fire-resistance temperature, mainly for back-up insulation of all refractory xonstructions.
SPECIFICATION AND TECHNICAL DATA
A . Chemical Analysis
SiO2……………… 47-48%
CaO ……………… 44-45%
Al2O3 …………… 0.3-0.4%
MgO………………… 0.5--0.7%
Fe2O3 ……………… 0.3--0.4%
Na2-K2O ………… 0.9--0.12%
Lgnition loss(mainly H2O)…… 6--7%
B. Our Standard GB/T10699-1998 TYPE-1998Ⅱ
Reference Standard Europe Standard) EN1094-6-1998
ITEM | Unit | YONGDA BRAND | GB/T10699 -1998 TYPE-Ⅱ | |||
HCS-23H | HCS-25H | HCS-27H | HCS-30H | ≤220, ≤270 | ||
Bulk density | kg/m3 | 230 ±10% | 250 ±10% | 270 ±10% | 300 ±10% | ≤220, ≤270 |
Flexural Strength | MPa | ≥0.45 | ≥0.50 | ≥0.55 | ≥0.60 | ≥0.30 |
Compressive Strength | MPa | ≥0.8 | ≥0.9 | ≥1.0 | ≥1.1 | ≥0.50 |
Thermal Cond. | W/m.k | 200℃ 0.085 400℃ 0.100 600℃ 0.152 800℃ 0.214 | 200℃ 0.095 400℃ 0.108 600℃ 0.156 800℃ 0.216 | 200℃ 0.098 400℃ 0.110 600℃ 0.158 800℃ 0.218 | 200℃ 0.102 400℃ 0.116 600℃ 0.164 800℃ 0.226 | 100℃ 0.065 200℃ 0.075 300℃ 0.087 400℃ 0.100 |
Service Temp.Limit | ℃ | 1100 | 1100 | 1100 | 1100 | 1000 |
Linear Shrinkage (EN 1094-6-1998) | % | ≤2 (1050,12hrs) | ≤2 (1050,12hrs) | ≤2 (1050,12hrs) | ≤2 (1050,12h) | ≤2 (1000,16hrs) |
NOTE: No China Standard for 1100C ca-si-board at present,so we use Europe standard EN1094-6-1998 for linear shrinkage test,12h at 50℃ below max. service temp.